| Non-Ferrous Alloys Analysis Chart | FORD MOTOR CO. | Apprentice School Metalurgy Dept. | |||||||||
| Alloy Name | Copper | Tin | Zinc | Lead | Aluminum | Iron | Phosphorus | Antimony | Nickel | Total Impurities | |
| Red Bronze #1 | 80.5 - 84.5 | 4.0 - 5.0 | 6.0 - 8.0 | 5.0 - 7.0 | |||||||
| Red Bronze #2 | 75.0 - 79.0 | 1.0 - 2.0 | 14.0 - 18.0 | 2.0 - 4.0 | |||||||
| "A" Bronze | 93.5 - 94.5 | 5.0 - 5.5 | .40 - .60 | ||||||||
| "B" Bronze | 88.0 - 91.5 | 4.5 - 5.5 | 3.25 - 4.75 | ||||||||
| "O" Bronze | 90 | 10 | |||||||||
| "Z" Bronze | 85.0 - 89.0 | 7.5 - 8.5 | 2.25 - 4.25 | .75 - 1.75 | |||||||
| Aluminum Bronze | 89.5 - 90.5 | 9.5 - 10.5 | .25 Max | ||||||||
| #6 Phosphor Bronze | 77.0 - 82.0 | 9.0 - 10.0 | 8.0 - 11.0 | .70 - 1.0 | Not over 1% | ||||||
| #10 High Lead Bronze | 63.5 - 71.5 | 4.0 - 6.0 | 23.5 - 26.5 | Not over 1% | |||||||
| Manganese Bronze | 59.0 - 61.0 | .75 - 1.25 | 37.0 - 39.0 | .75 - 1.25 | Mn .15 - .35 | ||||||
| White Bronze | 53.5 - 54.5 | 28.25 - 29.25 | 2.25 - 3.25 | 14.0 - 15.0 | |||||||
| Tractor Worm Gear | 88.0 - 90.0 | 10.0 - 12.0 | .35 Max | .20 - .35 | Including Pb .75 Max | ||||||
| Journal Bearing Back | 75.0 - 80.0 | 7.0 - 8.0 | 10.0 - 15.0 | Not over 3% | |||||||
| #1 Red Brass | 82.0 - 90.0 | 7.0 - 10.0 | 3.0 - 4.0 | 2.0 - 4.0 | Not over 1/2% | ||||||
| "S" Brass | 64.0 - 66.0 | 34.0 - 36.0 | .30 Max | ||||||||
| "W" Brass | 60.0 - 63.0 | Balance | 2.25 - 3.25 | .10 Max | |||||||
| Yellow Brass | 65.0 - 70.0 | .5 - 2.0 | Balance | 4.0 - 6.0 | |||||||
| White Nickel Brass | 55.0 - 64.0 | Balance | .35 Max | 16.0 Min | .60 Max | ||||||
| Brass Die Casting | 54.0 - 60.0 | 1.0 - 3.0 | 36.0 - 42.0 | ||||||||
| Drawn White Nickel Brass | 45.0 - 49.0 | 35.0 - 39.0 | 2.0 - 4.0 | 13.0 - 15.0 | |||||||
| Low Brass | 70.0 - 72.0 | Balance | |||||||||
| Forging Brass | 56.0 - 60.0 | 36.0 - 40.0 | 2.0 Max | .25 Max | |||||||
| #12 Aluminum Alloy | 7.0 - 8.5 | Balance | 1.0 Max | ||||||||
| Crank Case Aluminum | 7.0 - 8.5 | 1.75 - 2.25 | 87.55 | Si Mn Sn Fe 1.70 Max | Other Impurities - 0 | ||||||
| Aluminum Alloy Die Casting | 9.25 - 10.75 | Balance | Si Mn Sn Fe 1.70 Max | Other Impurities - 0 | |||||||
| Close Grained Aluminum Casting | 11.0 - 13.50 | .20 Max | 85.5 Max | ||||||||
| #95-4 Aluminum Die Casting Alloy | 3.75 - 4.25 | .30 Max | 92.0 - 94.0 | 1.5 Max | .50 - .75 | Si .25 - .75 | |||||
| Babbitt | 7.0 - 7.5 | 85.0 - 86.0 | .10 Max | 7.0 - 7.5 | |||||||
| Babbitt (Lincoln) | 4.0 - 5.0 | 90.0 - 92.0 | .10 Max | 4.0 - 5.0 | |||||||
| Journal Bearing Lining | 4.0 - 5.0 | 85.0 - 86.0 | 8.0 Min | ||||||||
| Zinc Die Casting Metal | 2.5 - 3.5 | Balance | .03 Max | 3.5 - 4.5 | .02 Max | Cd .04 Max | .10 Max | ||||
| D - 215 - F | |||||||||||